SJ type anti-corrosion pumping agent
1. Product introduction
SJ type anti-corrosion pumping agent conforms to the national industry standard of JC/T1011-2006, and the product quality has passed the test of the National Quality Inspection Center and the Liaoning Building Materials Product Quality Center. The products have been used in high-performance concrete, anti-corrosion and anti-corrosion concrete, air-tight concrete, anti-chloride ion diffusion-resistant concrete and anti-cracking, anti-seepage, anti-freezing, anti-carbonation, anti-abrasion of railway, highway, marine engineering, hydraulic engineering, chemical industry, etc. , commodity pumping, widely used in ordinary concrete, and achieved significant technical, economic and social benefits.
2. The main purpose of the product
SJ type anti-corrosion pumping agent is suitable for gypsum eroded by sulfate, magnesium salt, salt crystal, sulfuric acid acid, dissolution type (including carbonic acid type) with various acidic media, harmful gas and chloride ion penetration, diffusion and migration properties. Strata, salt-bearing strata, magnesium saline soil, coal-measure strata with high water pressure leakage, gypsum rock strata, carbonate strata, saline salt rock strata, saline salt lake, seawater chloride corrosion, toxic and harmful (gas) gas Concrete engineering of infiltrated railway, highway, marine engineering, tunnel and bridge; concrete engineering with high concentration of CO2 in groundwater, acid rain, industrial and domestic wastewater; activated aggregate concrete engineering with active expansion rate of alkali aggregate ≥ 0.1%; Leaked toxic and flammable gases, petrochemical concrete projects; high-volume, high-strength, and high-performance concrete projects with high impermeability and high crack resistance; can also be used in hydropower stations, dams, spillways, reservoirs, civil air defense, basements , Impermeability and crack-resistant concrete and mortar engineering and high-performance concrete engineering of overpass, highway pavement, airstrip, rigid roof level, toilet, kitchen.
3. Main types of products
SJ type anti-corrosion pumping agent is a liquid product. The dosage is 2.5~3.0% of cementitious material. It has the functions of preventing and adsorbing corrosive media, reducing shrinkage and cracking, compacting and anti-seepage, plasticizing, water-reducing, air-entraining, pumping, Enhancement, anti-corrosion, anti-freezing, inhibiting the active reaction of alkali aggregate, inhibiting rust and protecting ribs, etc.
4. Key points of product application technology
1. Use this product in accordance with Tie Jian [2005] No. 157 "Interim Regulations on Durability Design of Railway Concrete Structures", TB10120-2002, J160-2002 "Technical Specifications for Railway Gas Tunnels", GBJ82-85, GB/T2420-1981, JC /T1011-2006 "Concrete anti-sulfate corrosion preservative" standard.
2. Dosage: selected according to the nature of corrosion and the environment, the lower limit of the weak corrosion environment, the middle value of the moderate corrosion environment, the upper limit of the strong corrosion environment, the technical basis is selected according to the test results, the principle should be Not lower than the minimum value of the performance index in the technical standard.
3. Mixing method: This product can be mixed with cementitious material, sand, stone and water to mix and use evenly.
4. Mixing ratio design requirements: According to "Tie Jianshe Letter (2007) No. 1212 "High-performance Concrete Temporary Mixing Material Design Mixing Ratio"", SJ type anti-corrosion pumping agent is used. Strength grade: airtight concrete is C30~C35, anti-corrosion concrete is C25~C30; cement type is ordinary Portland cement ≥32.5R, anti-corrosion and anti-corrosion concrete can also choose slag cement, fly ash cement, pozzolan cement, When there is active reaction of alkali aggregate, ordinary Portland cement with alkali content < 0.6% and ≥ 32.5R should be used; in special cases, 15-25% grade I and II fly ash or 20-30% fly ash can be used The mixed slag powder or 5-10% silica powder will have better compound mixing effect; medium-coarse river sand should be used for sand, with a sand rate of 38-40% and a mud content of less than 2.0%; Crushed stone or pebbles, material diameter 5-25mm, mud content less than 1.0% or stone powder mud content less than 5.0%; using tap water, the water-binder ratio should be less than 0.45, and the air-tight concrete should be less than 0.40, the suitable water-binder ratio is 0.33-0.38, the slump value of concrete for pumping construction shall be 160-200mm, the water-cement ratio shall be reduced as much as possible, and the water consumption shall be determined according to the basic requirements of construction.
5. Pouring and vibrating: Forced mechanical agitation should be used for mixing, continuous pouring should minimize construction joints, and mechanical vibrating should be used. Bubble.
6. Maintenance: The anti-corrosion and anti-corrosion concrete must be continuously maintained for more than 14 days before the final setting is completed. Adequate maintenance of heat preservation and moisture is an important measure for anti-corrosion, anti-corrosion and air-tight concrete. Avoid construction below 5 °C and above 38 °C, and use maintenance One-time curing agent can significantly improve the durability of concrete's corrosion resistance, wear resistance, crack resistance, impermeability, frost resistance and airtightness.
7. The anti-corrosion pumping agent should be used on the basis of passing the test, and the optimal technical and economical mixing ratio should be determined.
5. Product performance indicators
SJ type anti-corrosion pumping agent: according to the standard GB2420-81, GB8076-2008, JC473-2001, Tiejian (2005) 160, 157 admixture testing. See table:
Test items
|
Performance |
Measured value |
||
Homogeneous |
Moisture content (%)≤ |
------- |
------- |
|
MgO content (%)≤ |
5.0 |
0.05 |
||
CL-content (%)≤ |
0.2 |
0.005 |
||
Total alkali content (%)≤ |
10 |
1.95 |
||
Slurry fluidity (mm)≥ |
240 |
260 |
||
Physical |
Water reduction rate (%) ≥ |
20 |
25.0 |
|
Air content (%)±1.0 |
4.5 |
4.5 |
||
Water rate ratio (%) |
Normal pressure≤ |
20 |
0 |
|
Pressure≤ |
90 |
20 |
||
Slump retention value mm |
30min≥ |
120 |
180 |
|
60min≥ |
100 |
150 |
||
Expansion % |
1 d≥ |
0.05 |
0.13 |
|
28d≤ |
0.6 |
0.29 |
||
Relative durability (200 times)%≥ |
80 |
95 |
||
Compressive strength ratio% |
7d≥ |
90 |
130 |
|
28d≥ |
100 |
120 |
||
Corrosion resistance |
Corrosion resistance coefficient (K)≥ |
0.85 |
0.98 |
|
Expansion coefficient (E)≤ |
1.5 |
1.0 |
||
Alkali aggregate active expansion rate% |
14d≤ |
0.1 |
0.02 |
|
Corrosion of steel bars |
Without |
Without |
Without |
Remarks: per m3 of concrete, the total amount of chloride ions brought into the admixture is ≤0.002kg, the total alkali content is ≤0.30kg, and the water-cement ratio of the slurry fluidity is 0.29.
6. Product packaging and storage
This product is packed in plastic ton barrels, 1000±5kg per barrel, sunscreen, anti-breakage, warehouse storage, shelf life is 180 days, expired products should be tested before they can be used.
Shenyang Shenjia Technology Development Co., Ltd
Copyright © 2022 shenjiakj.com All Rights Reserved
Powered by:300.cn Shenyang 辽ICP备17007651号 SEO tag
Add:Zhangjiabao village, dengshibao Town, Faku County, Liaoning Province
Mobile phone:13998871793 15840105001
Tel:024-87050538 13002457357
QQ:1341489377
E-mail:1341489377@qq.com sj13002457357@163.com
Follow us